Search Results
A New Route to Highly Stretchable and Soft Inorganic–Organic Hybrid Elastomers Using Polydimethylsiloxane as Crosslinker of Epoxidized Natural Rubber
2021, Banerjee, Shib Shankar, Banerjee, Susanta, Wießner, Sven, Janke, Andreas, Heinrich, Gert, Das, Amit
Sulfur or peroxide crosslinking is the most common and conventional method to develop elastomeric materials. A new approach to crosslink epoxidized natural rubber (ENR) by aminopropyl terminated polydimethylsiloxane (AT-PDMS) is described, intending to develop a new kind of hybrid organic–inorganic elastomers. The curing reaction is accelerated by using hydroquinone as a catalyst. The formation of the hybrid structure is evident from the appearance of two glass transition temperatures, at −1 and −120 °C, for the ENR and PDMS phases, respectively. The curing reaction is found to be of first order with respect to amine concentration with the estimated activation energy of ≈62 kJ mol−1. Comparing the mechanical properties to a typical ENR-sulfur system leads to the conclusion that the ENR/AT-PDMS hybrid structure is highly stretchable and soft, as demonstrated by its relatively higher strain at failure (up to ≈630%), and lower hardness and modulus values. The higher stretchability and soft nature of the material are achieved by introducing flexible PDMS chains during the curing process resulting to a hybrid elastomer networks. This kind of soft but robust materials can find several applications in diverse fields, such as soft robotics, flexible, and stretchable electronics.
Ferric Ions Crosslinked Epoxidized Natural Rubber Filled with Carbon Nanotubes and Conductive Carbon Black Hybrid Fillers
2022-10-18, Damampai, Kriengsak, Pichaiyut, Skulrat, Stöckelhuber, Klaus Werner, Das, Amit, Nakason, Charoen
Natural rubber with 50 mol % epoxidation (ENR-50) was filled with carbon nanotubes (CNTs) and conductive carbon black (CCB) hybrid fillers with various CCB loadings of 2.5, 5.0, 7.0, 10.0 and 15.0 phr, and the compounds were mixed with ferric ion (Fe3+) as a crosslinking agent. The ENRs filled exclusively with CNTs, and CNT–CCB hybrid fillers exhibited typical curing curves at different CCB loadings, i.e., increasing torque with time and thus crosslinked networks. Furthermore, the incorporation of CNT–CCB hybrid fillers and increasing CCB loadings caused an enhancement of tensile properties (modulus and tensile strength) and crosslink densities, which are indicated by the increasing torque difference and the crosslink densities. The crosslink densities are determined by swelling and temperature scanning stress relaxation (TSSR). Increasing CCB loadings also caused a significant improvement in bound rubber content, filler–rubber interactions, thermal resistance, glass transition temperature (Tg) and electrical conductivity. A combination of 7 phr CNT and CCB with loading higher than 2.5 phr gave superior properties to ENR vulcanizates. Furthermore, the secondary CCB filler contributes to the improvement of CNT dispersion in the ENR matrix by networking the CNT capsules and forming CNT–CCB–CNT pathways and thus strong CNT–CCB networks, indicating the improvement in the tensile properties, bound rubber content and dynamic properties of the ENR composites. Moreover, higher electrical conductivity with a comparatively low percolation threshold of the hybrid composites was found as compared to the ENR filled with CNTs without CCB composite. The superior mechanical and other properties are due to the finer dispersion and even distribution of CNT–CCB hybrid fillers in the ENR matrix.