Interaction between the components in Tm-Cr-Ge system at 1070 K
The phase equilibrium diagram of the Tm-Cr-Ge ternary system was constructed at a temperature 1070 K based on the results of X-ray phase, microstructural analyzes and energy-dispersive X-ray spectroscopy in the whole concentration range. At the temperature of investigation, two new ternary compounds are realized in the system: TmCr6Ge6 (SmMn6Sn6 structure type, space group P6/mmm, a=0.51506(1), c=0.82645(2) nm) and Tm4Cr4Ge7 (Zr4Co4Ge7 structure type, space group I4/mmm, а=1.39005(9), с=0.54441(1) nm). Inclusion of Cr atoms in the structure of the binary germanide TmGe2 (structure type ZrSi2) up to 10 at. % Cr leads to the formation of a solid solution TmCrxGe2 (x = 0-0.33).
Phase equilibrium diagram of Y-Cu-Sb system at 870 K
The interaction of the components in the Y-Cu-Sb ternary system was investigated using the methods of X-ray phase analysis, microstructure, and energy-dispersive X-ray spectroscopy in the whole concentration range at 870 K. At the temperature of investigation Y-Cu-Sb system is characterized by the formation of three ternary compounds: Y3Cu22Sb9 (Dy3Cu20+xSb11-x structure type, space group F-43m, a=1.6614(3) nm), Y3Cu3Sb4 (Y3Au3Sb4 structure type, space group I-43d, а = 0.95357(5) nm), YCuSb2 (HfCuSi2 structure type, space group P4/nmm, a = 0.42580(1), c = 0.98932(3) nm). The solubility of copper in the binary compound YSb (NaCl structure type) extends up to 8 at. %.