Efficiency of Magnetostatic Protection Using Nanostructured Permalloy Shielding Coatings Depending on Their Microstructure

Abstract

The effect of microstructure on the efficiency of shielding or shunting of the magnetic fluxby permalloy shields was investigated in the present work. For this purpose, the FeNi shieldingcoatings with different grain structures were obtained using stationary and pulsed electrodeposition.The coatings’ composition, crystal structure, surface microstructure, magnetic domain structure, andshielding efficiency were studied. It has been shown that coatings with 0.2–0.6μm grains have adisordered domain structure. Consequently, a higher value of the shielding efficiency was achieved,but the working range was too limited. The reason for this is probably the hindered movement of thedomain boundaries. Samples with nanosized grains have an ordered two-domain magnetic structurewith a permissible partial transition to a superparamagnetic state in regions with a grain size of lessthan 100 nm. The ordered magnetic structure, the small size of the domain, and the coexistenceof ferromagnetic and superparamagnetic regions, although they reduce the maximum value ofthe shielding efficiency, significantly expand the working range in the nanostructured permalloyshielding coatings. As a result, a dependence between the grain and domain structure and theefficiency of magnetostatic shielding was found.