Einschmelzverhalten in den Systemen SiO2-K2CO3-CaMg(CO3)2 und SiO2-K2CO3-PbO

Abstract

Melting reactions were followed by means of simultaneous thermal analysis (STA with DTA, TGΑ and DTG) as well as x-ray diffraction. Α reaction sequence model was set up for the composition 80 SiO2-20 K2O which took especial note of the rate of CO2 evolution. Melting behaviour in the System SiO2-K2CO3-CaMg(CO3)2 is definitely controlled by the formation of an initial melt formed by reaction between K2CO3 AND SiO2. Similar findings hold for the SiO2-K2CO3-PbO system. Here the ternary silicate K2O · 2PbO · 2 SiO2 occurs from 420 °C. PbO is completely dissolved in the potash-rich silicate melt up to 650 °C. Use of red lead instead of litharge gives essentially the same results. Die Einschmelzreaktionen werden mit der Simultan-Thermoanalyse (STA mit DTA, TG, DTG) und der Röntgenbeugung untersucht. Für eine Zusammensetzung 80 SiO2—20 K2O wird ein Reaktionsfolgemodell aufgestellt, das insbesondere das Verhalten des sich abspaltenden CO2 berücksichtigt. Das Einschmelzverhalten im System SiO2-K2CO3-CaMg(CO3)2 ist maßgeblich von der Bildung einer Erstschmelze als Reaktionsprodukt zwischen SiO2 und K2CO3 abhängig. Ähnliches gilt für das System SiO2-K2CO3-PbO. Hier tritt von 420 °C ab das ternäre Silicat K2O · 2 PbO · 2 SiO 2 auf. PbO liegt bis 650 °C vollständig gelöst in der K2O-reichen Silicatschmelze vor. Bei Einsatz von Pb3O4 als Bleiträger ist ein im wesentlichen ähnliches Verhalten wie bei Einsatz von PbO festzustellen.