6 results
Search Results
Now showing 1 - 6 of 6
- ItemMicrostructure, Texture, and Strength Development during High-Pressure Torsion of CrMnFeCoNi High-Entropy Alloy(Basel : MDPI, 2020) Skrotzki, Werner; Pukenas, Aurimas; Odor, Eva; Joni, Bertalan; Ungar, Tamas; Völker, Bernhard; Hohenwarter, Anton; Pippan, Reinhard; George, Easo P.The equiatomic face-centered cubic high-entropy alloy CrMnFeCoNi was severely deformed at room and liquid nitrogen temperature by high-pressure torsion up to shear strains of about 170. Itsmicrostructurewas analyzed by X-ray line profile analysis and transmission electronmicroscopy and its texture by X-ray microdiffraction. Microhardness measurements, after severe plastic deformation, were done at room temperature. It is shown that at a shear strain of about 20, a steady state grain size of 24 nm, and a dislocation density of the order of 1016 m-2 is reached. The dislocations are mainly screw-type with low dipole character. Mechanical twinning at room temperature is replaced by a martensitic phase transformation at 77 K. The texture developed at room temperature is typical for sheared face-centered cubic nanocrystalline metals, but it is extremely weak and becomes almost random after high-pressure torsion at 77 K. The strength of the nanocrystalline material produced by high-pressure torsion at 77 K is lower than that produced at room temperature. The results are discussed in terms of different mechanisms of deformation, including dislocation generation and propagation, twinning, grain boundary sliding, and phase transformation. © 2020 by the authors. Licensee MDPI, Basel, Switzerland.
- ItemEffect of Stacking Fault Energy on Microstructure and Texture Evolution during the Rolling of Non-Equiatomic CrMnFeCoNi High-Entropy Alloys(Basel : MDPI, 2020) Dan Sathiaraj, G.; Kalsar, Rajib; Suwas, Satyam; Skrotzki, WernerThe evolution of microstructure and texture in three non-equiatomic CrMnFeCoNi high-entropy alloys (HEAs) with varying stacking fault energy (SFE) has been studied in up to 90% rolling reductions at both room and cryogenic temperature. All the HEAs deform by dislocation slip and additional mechanical twinning at intermediate and shear banding at high rolling strains. The microstructure is quite heterogeneous and, with strain, becomes highly fragmented. During rolling, a characteristic brass-type texture develops. Its strength increases with a decreasing SFE and the lowering of the rolling temperature. The texture evolution is discussed with regard to planar slip, mechanical twinning, and shear banding. © 2020 by the authors. Licensee MDPI, Basel, Switzerland.
- ItemRevealing Grain Boundary Sliding from Textures of a Deformed Nanocrystalline Pd–Au Alloy(Basel : MDPI, 2018-1-25) Toth, Laszlo S.; Skrotzki, Werner; Zhao, Yajun; Pukenas, Aurimas; Braun, Christian; Birringer, RainerEmploying a recent modeling scheme for grain boundary sliding [Zhao et al. Adv. Eng. Mater. 2017, doi:10.1002/adem.201700212], crystallographic textures were simulated for nanocrystalline fcc metals deformed in shear compression. It is shown that, as grain boundary sliding increases, the texture strength decreases while the signature of the texture type remains the same. Grain boundary sliding affects the texture components differently with respect to intensity and angular position. A comparison of a simulation and an experiment on a Pd–10 atom % Au alloy with a 15 nm grain size reveals that, at room temperature, the predominant deformation mode is grain boundary sliding contributing to strain by about 60%.
- ItemTi/Al multi-layered sheets: Differential speed rolling (Part B)(Basel : MDPI, 2016) Romberg, Jan; Freudenberger, Jens; Watanabe, Hiroyuki; Scharnweber, Juliane; Eschke, Andy; Kühn, Uta; Klauß, Hansjörg; Oertel, Carl-Georg; Skrotzki, Werner; Eckert, Jürgen; Schultz, LudwigDifferential speed rolling has been applied to multi-layered Ti/Al composite sheets, obtained from accumulative roll bonding with intermediate heat treatments being applied. In comparison to conventional rolling, differential speed rolling is more efficient in strengthening the composite due to the more pronounced grain refinement. Severe plastic deformation by means of rolling becomes feasible if the evolution of common rolling textures in the Ti layers is retarded. In this condition, a maximum strength level of the composites is achieved, i.e., an ultimate tensile strength of 464 MPa, while the strain to failure amounts to 6.8%. The deformation has been observed for multi-layered composites. In combination with the analysis of the microstructure, this has been correlated to the mechanical properties.
- ItemPhase Transformation Induced by High Pressure Torsion in the High-Entropy Alloy CrMnFeCoNi(Basel : MDPI, 2022) Chulist, Robert; Pukenas, Aurimas; Chekhonin, Paul; Hohenwarter, Anton; Pippan, Reinhard; Schell, Norbert; Skrotzki, WernerThe forward and reverse phase transformation from face-centered cubic (fcc) to hexagonal close-packed (hcp) in the equiatomic high-entropy alloy (HEA) CrMnFeCoNi has been investigated with diffraction of high-energy synchrotron radiation. The forward transformation has been induced by high pressure torsion at room and liquid nitrogen temperature by applying different hydrostatic pressures and large shear strains. The volume fraction of hcp phase has been determined by Rietveld analysis after pressure release and heating-up to room temperature as a function of hydrostatic pressure. It increases with pressure and decreasing temperature. Depending on temperature, a certain pressure is necessary to induce the phase transformation. In addition, the onset pressure depends on hydrostaticity; it is lowered by shear stresses. The reverse transformation evolves over a long period of time at ambient conditions due to the destabilization of the hcp phase. The effect of the phase transformation on the microstructure and texture development and corresponding microhardness of the HEA at room temperature is demonstrated. The phase transformation leads to an inhomogeneous microstructure, weakening of the shear texture, and a surprising hardness anomaly. Reasons for the hardness anomaly are discussed in detail.
- ItemTi/Al multi-layered sheets: Accumulative roll bonding (Part A)(Basel : MDPI, 2016) Romberg, Jan; Freudenberger, Jens; Bauder, Hansjörg; Plattner, Georg; Krug, Hans; Holländer, Frank; Scharnweber, Juliane; Eschke, Andy; Kühn, Uta; Klauß, Hansjörg; Oertel, Carl-Georg; Skrotzki, Werner; Eckert, Jürgen; Schultz, LudwigCo-deformation of Al and Ti by accumulative roll bonding (ARB) with intermediate heat treatments is utilized to prepare multi-layered Ti/Al sheets. These sheets show a high specific strength due to the activation of various hardening mechanisms imposed during deformation, such as: hardening by grain refinement, work hardening and phase boundary hardening. The latter is even enhanced by the confinement of the layers during deformation. The evolution of the microstructure with a special focus on grain refinement and structural integrity is traced, and the correlation to the mechanical properties is shown.