2013, Müller, Michael Thomas, Dreyße, Janine, Häußler, Liane, Krause, Beate, Pötschke, Petra

Linear low-density polyethylene (LLDPE) was melt-mixed with multiwalled carbon nanotubes (MWCNTs) and varying amounts of three different kinds of talc (phyllo silicate), each with a different particle size distribution, to examine the effect of these filler combinations with regards to the electrical percolation behavior. The state of the filler dispersion was assessed using transmission light microscopy and electron microscopy. The use of talc as a second filler during the melt mixing of LLDPE/MWCNT composites resulted in an improvement in the dispersion of the MWCNTs and a decrease of the electrical percolation threshold. Talc with lower particle sizes showed a more pronounced effect than talc with larger particle sizes. However, the improvement in dispersion was not reflected in the mechanical properties. Modulus and stress values increase with both, MWCNT and talc addition, but not in a synergistic manner. The crystallization behavior of the composites was studied by differential scanning calorimetry to determine its potential influence on the electrical percolation threshold. It was found that the crystallinity of the matrix increased slightly with the addition of talc but no further increments were observed with the incorporation of the MWCNTs. © 2013 Wiley Periodicals, Inc.

2013, Pötschke, Petra, Krause, Beate, Buschhorn, Samuel T., Köpke, Ulf, Müller, Michael T., Villmow, Tobias, Schulte, Karl

The paper reports the effect of using of a three roll mill as additional dispersion step after twin-screw melt extrusion of nanocomposites containing thermoplastic polymers and multiwalled carbon nanotubes. The three roll milling technology was adapted to elevated temperatures of up to 180 °C and examples are shown for its use in processing of different pre-compounded thermoplastic polymer composites based on polypropylene, polycaprolactone and ethylene-vinyl acetate. The aim is to enhance the state of dispersion achieved by the previous melt extrusion step. In particular, depending on the state of dispersion before three roll milling and the adapted conditions, like number of runs and gap sizes, a reduction of number and size of remaining primary nanotube agglomerates was found. This was studied using light microscopy. The resulting improvements in mechanical properties were assessed and could be attributed to the improved dispersion. In some cases agglomerate free samples could be achieved after the three roll milling process. © 2012 Elsevier Ltd.