    Antibacterial Ti-Cu alloy with enhanced mechanical properties as implant applications
    (Bristol : IOP Publishing, 2020) Yi, ChangBo; Ke, ZunYun; Zhang, Lei; Tan, Jun; Jiang, YeHua; He, ZhengYuan
    The service life as hard tissue implantation for clinical application needs compatible mechanical properties, e.g. strength, modulus, etc, and certain self-healing in case of internal infection. Therefore, for sake of improving the properties of Ti-Cu alloy, the microstructure, mechanical properties, corrosion resistance and antibacterial properties of Ti-xCu alloy (x = 2, 5, 7 and 10 wt.%) prepared by Ar-arc melting followed by heat treatment were studied. The results show that the Ti-Cu alloy was mainly composed of α-Ti matrix and precipitated Ti2Cu phase. The Cu element mainly accumulates in the lamellar structure and forms the precipitated Ti2Cu phase. As the increase of Cu content, the lamellar Ti2Cu phase increases, the compressive strength and elastic modulus also were altered. The Ti-7Cu alloy exhibited the higher compressive strength (2169 MPa) and the lower elastic modulus (108 GPa) compared with other Ti-Cu alloys. The corrosion resistance of Ti-xCu alloys increases with the increase of Cu content. When the Cu content was greater than 5 wt.%, the value of corrosion current density for Ti-Cu alloy was less than 1 μAcenterdotcm−2, which is also significantly lower than that of CP-Ti. The antibacterial test revealed that only the Ti-Cu alloy with 5 wt.% or greater Cu content could display a strong antibacterial rate against E. coli and S. aureus. Therefore, the prepared Ti-7Cu alloy via heat treatment showed excellent mechanical properties, corrosion resistance, and antibacterial properties, which would meet the replacement of human hard tissue and clinical applications.
  • Thumbnail Image
    Item
    Phase Formation, Microstructure and Mechanical Properties of Mg67Ag33 as Potential Biomaterial
    (Basel : MDPI, 2021) Kosiba, Konrad; Prashanth, Konda Gokuldoss; Scudino, Sergio
    The phase and microstructure formation as well as mechanical properties of the rapidly solidified Mg67Ag33 (at. %) alloy were investigated. Owing to kinetic constraints effective during rapid cooling, the formation of equilibrium phases is suppressed. Instead, the microstructure is mainly composed of oversaturated hexagonal closest packed Mg-based dendrites surrounded by a mixture of phases, as probed by X-ray diffraction, electron microscopy and energy dispersive X-ray spectroscopy. A possible non-equilibrium phase diagram is suggested. Mainly because of the fine-grained dendritic and interdendritic microstructure, the material shows appreciable mechanical properties, such as a compressive yield strength and Young’s modulus of 245 ± 5 MPa and 63 ± 2 GPa, respectively. Due to this low Young’s modulus, the Mg67Ag33 alloy has potential for usage as biomaterial and challenges ahead, such as biomechanical compatibility, biodegradability and antibacterial properties are outlined.
  • Thumbnail Image
    Item
    Efficiency of Magnetostatic Protection Using Nanostructured Permalloy Shielding Coatings Depending on Their Microstructure
    (Basel : MDPI, 2021) Zubar, T.; Grabchikov, S.; Kotelnikova, A.; Kaniukov, E.; Kutuzau, M.; Leistner, K.; Nielsch, K.; Vershinina, T.; Tishkevich, D.; Kanafyev, O.; Kozlovskiy, A.; Zdorovets, M.; Fedosyuk, V.; Trukhanov, A.
    The effect of microstructure on the efficiency of shielding or shunting of the magnetic fluxby permalloy shields was investigated in the present work. For this purpose, the FeNi shieldingcoatings with different grain structures were obtained using stationary and pulsed electrodeposition.The coatings’ composition, crystal structure, surface microstructure, magnetic domain structure, andshielding efficiency were studied. It has been shown that coatings with 0.2–0.6μm grains have adisordered domain structure. Consequently, a higher value of the shielding efficiency was achieved,but the working range was too limited. The reason for this is probably the hindered movement of thedomain boundaries. Samples with nanosized grains have an ordered two-domain magnetic structurewith a permissible partial transition to a superparamagnetic state in regions with a grain size of lessthan 100 nm. The ordered magnetic structure, the small size of the domain, and the coexistenceof ferromagnetic and superparamagnetic regions, although they reduce the maximum value ofthe shielding efficiency, significantly expand the working range in the nanostructured permalloyshielding coatings. As a result, a dependence between the grain and domain structure and theefficiency of magnetostatic shielding was found.