Nonlinear Thermopower Behaviour of N-Type Carbon Nanofibres and Their Melt Mixed Polypropylene Composites

Abstract

The temperature dependent electrical conductivity σ (T) and thermopower (Seebeck coeffi-cient) S (T) from 303.15 K (30◦ C) to 373.15 K (100◦ C) of an as-received commercial n-type vapour grown carbon nanofibre (CNF) powder and its melt-mixed polypropylene (PP) composite with 5 wt.% of CNFs have been analysed. At 30◦ C, the σ and S of the CNF powder are ~136 S m−1 and −5.1 µV K−1, respectively, whereas its PP/CNF composite showed lower conductivities and less negative S-values of ~15 S m−1 and −3.4 µV K−1, respectively. The σ (T) of both samples presents a dσ/dT < 0 character described by the 3D variable range hopping (VRH) model. In contrast, their S (T) shows a dS/dT > 0 character, also observed in some doped multiwall carbon nanotube (MWCNT) mats with nonlinear thermopower behaviour, and explained here from the contribution of impurities in the CNF structure such as oxygen and sulphur, which cause sharply varying and localized states at approximately 0.09 eV above their Fermi energy level (EF).

Description
Keywords
Carbon nanofibers, N-type polymer composites, Polypropylene, Thermoelectric properties, Variable range hopping
Citation
Paleo, A. J., Krause, B., Cerqueira, M. F., Muñoz, E., Pötschke, P., & Rocha, A. M. (2022, January). Nonlinear Thermopower Behaviour of N-Type Carbon Nanofibres and Their Melt Mixed Polypropylene Composites (Basel : MDPI). Basel : MDPI. https://doi.org//10.3390/polym14020269
Collections
License
CC BY 4.0 Unported