Some aspects of the workability of glass melts

Abstract

Criteria are given for the isothermal or isochomal workability of glass melts and discussed by means of a schematic example which is based on numerous measurements. A thesis for a simple connection of this kind of workability is presented and examined by means of so far existing measurements. The isothermal or isochomal workability, which becomes more important with increasing deformation rate, is in contrast to the non-isothermal or athermal workability. The differences are based on certain connections between the stiffness, the relaxation modulus of a glass melt, its high-temperature fracture strength and the value of the quantity Β in the Vogel-Fulcher-Tammann (VFT) equation if the constants are evaluated from a measurement of the whole viscosity-temperature range, from 101.5 to 1012 Pa s. Es werden einige Kriterien für die isotherme oder isochome Verarbeitbarkeit von Glasschmelzen gegeben, die an Hand eines schematischen Beispiels, das auf zahlreichen Messungen basiert, diskutiert werden. Eine These bezüglich eines einfachen Zusammenhangs dieser Art der Verarbeitbarkeit wird gegeben und an Hand bisher vorliegender Messungen geprüft. Diese isotherme oder isochome Verarbeitbarkeit, die um so mehr an Bedeutung gewinnt, je größer die Verformungsgeschwindigkeit wird, steht im Gegensatz zur nichtisothermen bzw. athermischen Verarbeitbarkeit. Die Unterschiede basieren auf bestimmten Zusammenhängen zwischen der Steifigkeit, dem Relaxationsmodul, der Hochtemperaturfestigkeit und der Größe Β aus der Vogel-Fulcher-Tammann (VFT)-Gleichung, wenn die Konstanten der VFT-Gleichung aus Messungen über den gesamten Viskositäts-Temperaturbereich von 101.5 bis 1012 Pa s ermittelt worden sind.