Weathering of tin oxide coated glass with low IR emissivity

Abstract

The weathering of K-glass has been studied by measuring transmission and reflection in the visible (VIS), near infrared (NIR) and infrared (IR) wavelength ranges, by chemical depth profiling with secondary neutral mass spectrometry (SNMS) and by atomic force microscopy (AFM) imaging. K-glass is a commercial tin oxide coated glass with low IR emissivity. The SnO2:F-coated side has been exposed to atmospheric conditions for up to 32 weeks and for up to two years. It could be shown that the optical properties are only affected in the VIS range, but the visible contamination does not influence the high IR reflection. This means that the heat-insulating properties of window glazings with the K-glass coating on the surface do not degrade under atmospheric conditions. Chemical depth profiles did not reveal major changes, except for an increase in the signals of minor elements on the surface, namely sodium, carbon and silicon. AFM showed that after 32 weeks the deep valleys of the rather rough crystalline SnO2:F are partially filled up. The high transmission of new K-glass can be regained since contamination or corrosion products can be removed by washing. The coating itself is chemically stable.