Physikalische Eigenschaften einiger Schwermetallfluoridgläser

Abstract

Thirteen glasses with ZrF4 as network former and BaF2, LaFß, YF3, AIF3, or NaF as other components were formed from the melt. Their densities, transformation temperatures, devitrification temperatures and thermal expansions were measured and their infra red spectra determined. The properties depend on the content of the particular component, e.g. LaFs, BaF2 or NaF, from which the structural action of these components in the glass may be determined. On a fabrique à partir de fontes de verre, 13 verres renfermant ZrF4 comme formateur de reseau et BaF2, LaFs, YF3, AIF3 ou NaF comme autres constituants. On a mesure leurs masses volumiques, leurs temperatures de transition vitreuse et de cristallisation et leurs coefficients de dilatation thermique lineaire. On a determine les spectres infrarouges de ces verres. Les proprietes dependent de la teneur de chaque composant pris separement, par exemple LaF3, BaF2 ou NaF, d'ou decoule l'influence structurale de ces derniers dans les verres. Es wurden 13 Gläser, die ZrF4 als Netzwerkbildner und BaF2, LaF3, YF3, AlF3 oder NaF als weitere Komponenten enthielten, aus der Schmelze hergestellt. An ihnen wurden Eigenschaften wie Dichte, Transformations- und Kristallisationstemperatur sowie linearer Wärmeausdehnungskoeffizient gemessen und die IR-Spektren dieser Gläser bestimmt. Die Eigenschaften sind vom Gehalt der einzelnen Komponenten, z. B. LaF3, BaF2 oder NaF, abhängig, woraus sich die strukturelle Wirkung dieser Komponenten in den Gläsern ergibt.