study of structural modification in extruded and heat-treated lithium disilicate glasses by the method of radiation color centers chronospectroscopy

Abstract

Samples of extruded and non-extruded lithium disilicate glasses were studied. Extruded glass samples were cut out along and across the extrusion axis of fmished cylindrical rods. For all the samples, spectra of radiation-induced absorption, Δα(E), were measured for various time instants after the cessation of X-irradiation. On the data basis obtained, kinetic dependences. Δα = f(t), were plotted and analyzed. In the diagram "Δα versus lgt", they are represented by straight hnes. Each of them is falling down with its own constant slope a. These a's are rate parameters of the decay of radiation color centers (CCs). They appear to be functions of average distances between recombinating electron and hole CCs. The above α-parameter decreases when passing from the longitudinal cut extruded glass sample to the sample of the non-extruded glass and finally to the transversely cut extruded glass sample. These data mean that, in the course of extrusion, the glass structure becomes less dense in the axial direction of extruded glass rods and more dense in the radial one. Α 4-hour heat treatment at 465 °C (≈5°C above the glass transformation temperature, Tg) eliminated the above anisotropy of radiation properties in extruded glasses and forced their anisometric structures to return to the isometric State characteristic of the non-extruded glass.