Mechanical behaviour and environmental stability of continuous fibre-reinforced glass-ceramic matrix composites

Abstract

The mechanical behaviour of three continuous Silicon carbide fibre-reinforced glass-ceramic matrix composites has been investigated at room and high temperatures. Commercially available composites with magnesium aluminosilicate, calcium aluminosilicate and barium magnesium aluminosilicate glass-ceramic matrices were considered. The materials were tested in the as-received and aged (heat-treated in a n oxidizing environment) condition. Four-point bend static tests and fiexural creep, fatigue and creep-fatigue tests were carried out a s well as a small quantity of tensile tests of aged composites. The experimental results have highlighted the importance of the carbon-rich layer at the fibre/matrix interface for obtaining "graceful" failures. At temperatures of 700 to 800 °C oxidative degradation of the interface results in significant strength reduction and a transition to brittle fracture mode. By rapid heat treatment of the materials at 1100°C for 1 h it is possible to seal the fibre ends by forming a silica "plug" which prevents oxygen ingress, retaining the carbon-rich interphase and composite behaviour. The results of the creep and creep-fatigue tests indicate low-cycle loading has a strong influence on the life of components at high temperatures.